Abstract

The influence of different concentration of paraben on properties of chitosan/paraben composite films was studied. The structure characterizations of films were characterized by FT-IR and SEM. Transmittance, color, mechanical properties, water vapor permeability, swelling degree and antibacterial properties were also tested. Results: with the increasing of concentration of paraben, the transmittance of composite film decreased and the color became yellow. The highest tensile strength was 37.0 MPa, and the elongation at the break was 55% when the concentration of paraben were 5%(WT) and 25%(WT), respectively. The water vapor permeability was 7.5×10-14 g/(m2·s·Pa) when concentration of paraben was 5%(WT), in which case composite films witness a good swelling degree and gas barrier property. The antibacterial property of chitosan/paraben composite films on Staphylococcus aureus was better than on Escherichi coli,the maximum value of bacteriostatic circle diameter was 10.8 mm.

Publication Date

3-28-2016

First Page

131

Last Page

136

DOI

10.13652/j.issn.1003-5788.2016.03.029

References

[1] López O V, Giannuzzi L, Zaritzky N E, et al. Potassium sorbate controlled release from corn starch films[J]. Materials Science & Engineering C Materials for Biological Applications, 2013, 33(3):1 583-1 591.
[2] Gemili S, Yemenicioglu A, Altnkaya S A. Development of cellulose acetate based antimicrobial food packaging materials for controlled release of lysozyme[J]. Journal of Food Engineering, 2009, 90(4): 453-462.
[3] Sánchez-González L, Cháfer M, González-Martínez C, et al. Study of the release of limonene present in chitosan films enriched with bergamot oil in food simulants[J]. Journal of Food Engineering, 2011, 105(1): 138-143.
[4] Hu Chang-ying, Chen Mo, Wang Zhi-wei. Release of thymol, cinnamaldehyde and vanillin from soy protein isolate films into olive oil[J]. Packaging Technology & Science, 2012, 25(2): 97-106.
[5] Rodriguez F, Sepulveda H M, Bruna J, et al. Development of cellulose eco-nanocomposites with antimicrobial properties oriented for food packaging[J]. Packaging Technology & Science, 2013, 26(3): 149-160.
[6] Jipa I M, Stoica-Guzun A, Stroescu M. Controlled release of sorbic acid from bacterial cellulose based mono and multilayer antimicrobial films[J]. LWT - Food Science and Technology, 2012, 47(2): 400-406.
[7] Pintado C M B S, Ferreira M A S S, Sousa I. Control of pathogenic and spoilage microorganisms from cheese surface by whey protein films containing malic acid, nisin and natamycin[C]// 4th European Symposium of IAFP. [S.l.]: Food Control, 2008: 240-246.
[8] Ramos S L, Santos A C, Leo M V, et al. Antimicrobial activity of edible coatings prepared from whey protein isolate and formulated with various antimicrobial agents[J]. International Dairy Journal, 2012, 25(2): 132-141.
[9] Rocha M D, Loiko M R, Tondo E C, et al. Physical, mechanical and antimicrobial properties of Argentine anchovy (Engraulis anchoita) protein films incorporated with organic acids[J]. Food Hydrocolloids, 2014, 37(2): 213-220.
[10] 李学红. 环糊精在抗菌食品包装中的基础应用研究[D]. 无锡: 江南大学, 2007: 55-67.
[11] 屠洁, 刘冠卉, 李前龙, 等. 壳聚糖—甘油—丝素共混膜的制备及性能研究[J]. 食品与机械, 2010, 26(6): 34-36.
[12] Singh T P, Chatli M K, Sahoo J. Development of chitosan based edible films: process optimization using response surface methodology[J]. Journal of Food Science and Technology, 2014, 52(5): 2 530-2 543.
[13] 李崇高, 黄建初, 薛海波, 等. 改性葡甘聚糖/壳聚糖共混膜在甜玉米保鲜中的应用[J]. 食品与机械, 2013, 29(3): 202-205.
[14] Sangsuwan J, Rattanapanone N, Pongsirikul I. Development of active chitosan films incorporating potassium sorbate or vanillin to extend the shelf life of butter cake[J]. International Journal of Food Science and Technology, 2014, 50(2): 323-330.
[15] Hosseini M H, Razavi S H, Mousavi M A. Antimicrobial, physical and mechanical properties of chitosan-based films incorporsted with thyme, clove and cinnamon essential oils[J]. Journal of Food Processing & Preservation, 2010, 33(6): 727-743.
[16] 王竹天, 宋凤英, 高鹤娟. 食品中对羟基苯甲酸乙酯, 丙酯含量分析方法[J]. 中国食品卫生杂志, 1989(2): 27-29.
[17] 王金龙. 对羟基苯甲酸丁酯的安全性及其应用瓶颈[J]. 现代食品科技, 2009, 25(8): 960-963.
[18] 邹玉萍, 夏文水. 尼泊金酯对蒸煮袋熟鱼防腐保藏[J]. 食品与生物技术学报, 2009, 28(2): 167-171.
[19] 林忠洋, 马万里, 齐迹, 等. 对羟基苯甲酸酯类防腐剂的人体暴露[J]. 化学进展, 2015(5): 614-622.
[20] 刘慧, 徐诚, 刘倩, 等. 对羟基苯甲酸酯类内分泌干扰效应的研究进展[J]. 卫生研究, 2016(1): 155-158.
[21] Yu Wen-xi, Wang Zhi-wei, Hu Chang-ying, et al. Properties of low methoxyl pectin-carboxymethyl cellulose based on montmorillonite nanocomposite films[J]. International Journal of Food Science and Technology, 2014, 49(12): 2 592-2 601.
[22] ASTM. ASTM D1003-2011 Standard test method for haze and luminous transmittance of transparent plastics[S]. Philadelphia, PA: In annual book of ASTM standards, 2011.
[23] 钟宇. 葛根淀粉基可食性包装膜物化与抗菌性能的研究[D]. 上海: 上海交通大学, 2012: 57-96.
[24] ASTM. ASTM D882-02 Standard test method for tensile properties of thin plastic sheeting[S]. Philadelphia, PA: In Annual Book of ASTM Standards, 2002.
[25] Hernandez-Munoz P. Mechanical and water barrier properties of glutenin films influenced by storage time 60[J]. Journal of Agricultural and Food Chemistry, 2003, 52(1): 79-83.
[26] 王亚珍, 谢晶, 李立, 等. 壳寡糖对壳聚糖—明胶—壳寡糖三元复合膜的性能影响研究[J]. 食品工业科技, 2015, 36(8): 134-137.
[27] 张智宏, 程春生, 覃宇悦, 等. 壳聚糖/柠檬草精油复合膜的制备及性能研究[J]. 食品工业科技, 2013, 34(9): 150-153.
[28] 鲍文毅, 徐晨, 宋飞, 等. 纤维素/壳聚糖共混透明膜的制备及阻隔抗菌性能研究[J]. 高分子学报, 2015(1): 49-56.
[29] 陈国安, 杨凯, 彭昌亚, 等. 新型食品防腐剂——尼泊金酯[J]. 中国调味品, 2003(3): 31-36.

Share

COinS
 
 

To view the content in your browser, please download Adobe Reader or, alternately,
you may Download the file to your hard drive.

NOTE: The latest versions of Adobe Reader do not support viewing PDF files within Firefox on Mac OS and if you are using a modern (Intel) Mac, there is no official plugin for viewing PDF files within the browser window.